Thomas high temperature resistant magnet adhesive

Product name High temperature resistant magnet steel adhesivesù£THO4058ù¤
Outline It is double-component epoxy adhesive. With the property of temperature and weather resistant, it is easy and convenient to use for it solidifies fast at normal temperature and bonds well.
Applications This product is widely applied to the bonding of such materials as motor magnetic ring (magnetic coil), magnetic metal, ceramics and composite materials. It also applies to the bonding, sealing, filling, repairing and stopping of cracks between the materials as magnetic and steel and the magnet.
Features The A component is the tinted thick liquid, non-solid particle. The B component is in tinted paste shape.
Fast curing speed. At 25 ûãC, 1-3 hour it is at the early stage of curing, 18 hours later, it reaches its maximum bonding strength.
It cures during 40-60 minutes if put into heating oven of 80-100 û?
Being durable and resistant to ultraviolet light, once the bond has formed.
Being heat-resistant, it adapts to a wide range of temperature and bonds well under high temperature.
With moderate viscosity, the adhesive leaves no bubbles, making the surface smooth and bright.
Mix the two components in a certain proportion, apply it to the surface of the substrates directly, which makes it so convenient to use.
You'll see long term durability and resistance to moisture, chemicals, oils, and temperature extremes.
Non-toxic after solidification, though it is a little smelly.
Being stable, its shelf life is one and half a year.
The main technical parameters are as follows:
Heat resistance scopeùº-45 ûãCù¨+410 ûãC
Cementation intensity: Normal temperature: Tensile strengthû?5MPa; Shearing strengthû?3 MPa
At 200 ûãC: Tensile strength 3-4.5 MPa
Instruction 1. Clean the surface of the material, make sure they have no dust or oil on them, wait until they are dry.
2. Mix A and B in a proportion of 10: 1.2--1.5 to get perfect bonding result at fastest speed at 25 ûãC
3. Spread the mixture on the substrates, put them together and apply some strength on them, finally, let them dry for 2-4 hours.
4. If the surface of ceramics needs to be shaped after the coating, hot press molding or cold press molding should be applied when the adhesive is in its preliminary curing time.
Notes 1. Use another can or container to blend A with B. The tools used to get A and B should be different.
2. A and B should be mixed well.
3. It is necessary to keep it well ventilated and away from fire.
4. If it has contact with skin, you should wash thoroughly with soap and water.
5. It can be stored at well-ventilated places with low temperature, and keep them away from fire.
6. Cover the lip after using it.