Single Fiber Strength Tester

The single fibers are stretched to break on a constant elongation extensometer (CRE) under specified conditions. The values of tensile strength, elongation at break, elongation strength, and initial modulus of the specimen obtained from the load-elongation curve or the data display acquisition system are suitable for the tensile test of chemical fiber and natural fiber Stretch performance test.

Standards
GB/T21120 Synthetic fibers for cement, cement mortar and concrete
GB/T14337 Testing method for tensile properties of man-made staple fibers
ISO 5079 Textiles - Fibres - Determination of breaking force and elongation at break of individual fibres
GB/T13835.5 Test method for rabbit hair—Part 5:Breaking tenacity and elongation at break of single fibre
ASTM D3822(M) Standard test method for tensile properties of single textile fibers
JIS L1015 Testing methods for man-made staple fibres
ASTM D1294/2524/3106/3217/1445 Method of test for breaking tenacity of wool fiber bundles
DIN53843-2 Testing of textiles– Loop tensile test for staple fibres
ISO3060 Textiles Cotton fibres Determination of breaking tenacity of flat bundles
BS5116、BS 4029 Hexagon socket screws and wrench keys: metric series —Part 5: Specification for hexagon socket set screws with cup point

Technical Parameters

Items Standard
requirements Design
requirements Implementation
methods
Load range According to the maximum load
requirements of the specimen 0-100cN Outsourcing, pressure sensor
Load error ¯1% ≤¯1% Sensor validity
Load resolution 0.1cN 0.1cN Sensor accuracy
Elongation range 100mm 100mm Outsourcing,
displacement sensor
Elongation error 0.05,0.1mm ≤0.01 Sensor validity
Elongation resolution 0.1% 1% Sensor accuracy
Clamp distance 2-20mm 1-20mm Machining
Lower gripper descent speed 5-20mm/min 1-100mm/min Outsourcing, stepper motor
Lower gripper stroke 100mm 100mm Machining

Accessories
The device can indicate or record the load applied to the specimen and the corresponding elongation value; (Force sensor)
The device can make load-elongation curve; (Integrated software)
The gripper suitably holds a single fiber at the desired nominal gauge length; (Manual, pneumatic and electric. The pneumatic gripper avoids the influence of the measurement of the force sensor and also reduces the degree of damage to the special brittle material during the clamping process.)
The device has a different stretching speed; (Stepper motor)
The device is used to wet the fibers in a wet state experiment so that the fibers are immersed during the test without affecting the test results; (Containers)
The device is used to precisely calibrate the instrument.