Lowes Liquid Silicone Rubber Raw Material for Silicone Mold Statue

1.Applications of Lowes Liquid Silicone Rubber Raw Material for Silicone Mold Statue
A. Resin crafts, poly resin crafts, PU crafts, PU resin crafts, unsaturated resin crafts;
B. Plaster, Gypsum, Cement, and Concrete decoration;
C. Lighting ornaments, candles crafts;
D. Plastic toy, stationery gifts crafts industry;
E. A large statue Buddha, relief, statues Buddha, artifacts copied;
F. Furniture, furniture decorative materials, building decoration materials;
G. Large-scale cement mold, artificial fossils Factory, Europe component factory;
H. Simulation landscapes;
I. Animals and plants sculpture;
J. Sandstone crafts;
K. Model design, product exploitation.


2.Features of Lowes Liquid Silicone Rubber Raw Material for Silicone Mold Statue
A. All hardness from 15 to 40 shore A;
B. Good fluidity, good operability, good for pouring method;
C. Excellent mechanical properties, in particular tear strength and tensile strength;
D. Excellent flexibility, easy to demould.
E. High temperature resistance, high duplication times and repeated use.
F. Wide range of catalysts/curing agent/hardener for various applications and various requirements on the operation time or curing time.
G. Good cut-growth resistance;
H. High durometer hardness;
I. Low shrinkage;
J. Easy release;
K. Room temperature cure within 24 hours or Heat-accelerable cure ;


3. Datasheet of Lowes Liquid Silicone Rubber Raw Material for Silicone Mold Statue

Model NO· XB-725 XB-730 XB-735 XB-740
Mixing Ratio (by weight) 100:3 100:3 100:3 100:3
Appearance/Color Translucent/White Translucent/White Translucent/White Translucent/White
Hardness (Shore A) 25¯2 30¯2 35¯2 40¯2
Mixed viscosity(mPa·s) 16000¯500 20000¯500 20000¯500 18000¯500
Working Time(at 23℃/75℉, MINS) 30~40 30~40 30~40 30~40
Curing Time(at 23℃/75℉, HRS) 3~5 3~5 3~5 3~5
Tensile strength, Mpa ≥4.2 ≥4.0 ≥4.0 ≥3.9
Tear strength, KN/m ≥28.5 ≥25.2 ≥19.5 ≥19.5
Shrinkage, % <0.2 <0.2 <0.2 <0.2
Elongation at break,% ≥550 ≥480 ≥480 ≥300