High Wear-resistance TPEs

Fender-TTM TPU series (1090T series)

1. UL certified V0 grade polyether TPU:

UL94-V0 (1.5mm) flame retardant grade, fully support the conventional structural cable through the IEC60332-1-2 single vertical burning test;

2. High and low-temperature shrinkage rate, shrinkage rate ≤1% in high and low-temperature cycle test;

3. High security and reliability, support optic cable through various environmental tests and life tests:

Mold resistance

Authoritative certified mold-resistant materials: through the military standard mold resistance test (GJB150.10);

Hydrolysis resistance: Pass 1000/2000Hrs hydrolysis resistance test (different model) (85®C/85% RH, 1000/2000 Hrs);

High and low-temperature resistance: Wide temperature range for use, Pass 720Hrs high-temperature test (125®C, 720Hrs) and low-temperature destructive tests such as low-temperature winding (-50®C) and low-temperature shock (-50®C);

Acid and alkali resistant, oil resistant, chemical resistant: Pass various acid and alkali resistance, oil resistance and chemical resistance test (e.g: acid and alkali resistance: 23®C/168h, intensity change rate ≤ 30%, extended rate ≥100%; oil resistance: 70 ®C / 24h oil resistance test, strength, and elongation, change rate ≤ 30%);

UV resistant: Pass UL1581 UV test (720Hrs UV cycle test, strength, and elongation, retention rate ≥ 80%);

4.High wear resistance: Polar material, high cohesive energy, and wear resistance are much better than conventional low-smoke halogen-free polyolefin materials (LSZH).
Technical Data of High Wear-resistance TPEs
Technical Data Sheet Model
Material Properties Test Standard Test Condition Unit 2885F-ESU-1088S
General Characteristics Material Category - - -
Appearance(Light/Semi-matte/Frosted) - - -
Extrusion/Injection - - -
Physical Characteristics Hardness ISO 48 15S Shore A 85
Proportion ISO 1183 - g/cm± 0.951
Melt Index ISO 1133-1:2011 190℃/2.16kg g/10min 3.2
Brittle Temperature ISO 812 - ℃
Mechanical Properties Elongation ISO37:2017 200mm/min % 475
Tensile Strength ISO37:2017 200mm/min Mpa 14.5
Tearing Strength ISO34-1:2015 500mm/min KN/m
Hot Air Aging Elongation Retention Rate ISO37:2017 - %
Tensile Strength Retention Rate ISO37:2017 - %
Electrical Performance Volume Resistivity ASTM D257 - Ohm-cm
Permittivity ASTM D150 - -
Combustion Performance Vertical Burning Test UL 94 3.0/6.0mm -
Oxygen Index ASTM D2863 - %
Feature

As one of the most professional plastic compounding companies, we provide styrenic thermoplastic elastomer, thermoplastic compound, tpe elastomero termoplastico and etc. For more information, please feel free to contact us!