20/40-86MPA High Density Ceramic Proppant

20/40-86MPA High Density Ceramic Proppant
Product Specifications:
20/40  69-86Mpa   10000PSI - 12500PSI 
Size 20/40
Roundness and sphericity 0.8/0.8
Body density 1.78-1.92g /cm3
Apparent density 3.14-3.37g /cm3
Crush 10,000 PSI< 5.0
12,500 PSI< 10.0
Acid solubility Max 7
Turbidity Max 200FTU
The crushing rate of ceramsite sand is affected by the following factors:
1. Raw material quality: The raw material quality of ceramsite sand has a great influence on the crushing rate. If the raw material contains too many impurities, pores or hardness, it is more likely to break during the production process.
2. Production process: The production process of ceramsite sand will also affect the crushing rate. For example, parameters such as temperature, pressure, and sintering time during the production process will affect the strength and toughness of ceramsite sand, thereby affecting its breakage rate.
3. Equipment performance: The working performance of ceramsite sand production equipment, such as the mixing speed of the mixer, the pressure of the molding machine, etc., will affect the crushing rate of ceramsite sand.
4. Operation method: The skills and experience of the operator will also affect the crushing rate of ceramsite sand. For example, improper feeding speed, insufficient mixing time or excessive molding pressure may cause the ceramsite sand to break.
Therefore, to reduce the crushing rate of ceramsite sand, it is necessary to optimize and control it from many aspects such as raw material quality, production process, equipment performance and operation methods.